B23R080 Grain Oriented Electrical Steel

B23R080 Grain Oriented Electrical Steel

Silicon steel is available in two main types: grain-oriented electrical steel (GOES) and non-grain oriented electrical steel (NGOES).

B23r080 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B23R080 steel Mechanical Properties

Grade	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B23R080	353	326	12	195	19	96.5

NOTE:. A detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction

B23R080 electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	The minimum magnetic induction B8 （T）
B23R080	0.23	7.65	0.80	1.87

NOTE:. A detector according to GB / T3655-2008 (G-series and P-series), GB / T3789-2008 (R Series)
B. G-series and P-series samples were rolling direction, and incubated for 2 hours at 800 ℃ after the elimination of stress annealing the magnetic properties were tested
c. P17 / 50 represents the maximum magnetic flux density of 1.7T, a frequency of 50Hz, the unit kg sample of core loss.
d. B50 representation corresponds to a magnetic field strength of the magnetic induction 5000A / m when.